FlowTech™ CHT High Flow - CM2™ Nozzle
- Artikel nr. 31994
- Variations-id 16168
- EAN 0850041631615
- Producentens ArtNr M2907-08
Microswiss and Bondtech have partnered to bring the High Flow, Hardened Tip CM2™ nozzle to the FlowTech ecosystem. This new nozzle incorporates proprietary CHT technology, specifically designed to enhance the filament flow rate. Core of the nozzle is made of high-temperature Copper Chromium Zirconium and plated with an Electroless Nickel Plating. This special alloy retains its strength at much higher temperatures compared to a regular copper alloy. The tip of the nozzle is made of M2 Hardened High Speed Steel and coated with a special WS2 nonstick nano coating.
Microswiss and Bondtech have partnered to bring the High Flow, Hardened Tip CM2™ nozzle to the FlowTech ecosystem. This new nozzle incorporates proprietary CHT technology, specifically designed to enhance the filament flow rate. Core of the nozzle is made of high-temperature Copper Chromium Zirconium and plated with an Electroless Nickel Plating. This special alloy retains its strength at much higher temperatures compared to a regular copper alloy. The tip of the nozzle is made of M2 Hardened High Speed Steel and coated with a special WS2 nonstick nano coating.
CHT - CM2™ Nozzle Features:
- Copper Chromium Zirconium body
- Plated with an Electroless Nickel Plating
- M2 Hardened High Speed Steel insert
- Plated with an Electroless Nickel Plating
- Coated with nonstick nano WS2 coating.
- Coefficient of friction: 0.035
- Heat-treated hardness: 68 HRC
- High Flow CHT Technology
- The FlowTech nozzle, equipped with Bondtech CHT technology, can achieve a maximum volumetric flow rate of up to 50 mm³/sec
- More uniform layer deposition is achieved by splitting the filament flow into multiple chambers as it passes through the melt zone. This reduces gaps and weak points between layers
- Orifice size available: .4mm, .6mm, .8mm, 1.0mm
Made in Sweden by Bondtech
Assembled in USA by Microswiss